New High-Performance SiC Fiber Developed for Ceramic Composites

Sylramic-iBN fiber is a new type of small-diameter (10-mm) SiC fiber that was developed at the NASA Glenn Research Center and was recently given an R&D 100 Award for 2001. It is produced by subjecting commercially available Sylramic (Dow Corning, Midland, MI) SiC fibers, fabrics, or preforms to a specially designed high-temperature treatment in a controlled nitrogen environment for a specific time. It can be used in a variety of applications, but it currently has the greatest advantage as a reinforcement for SiC/SiC ceramic composites that are targeted for long-term structural applications at temperatures higher than the capability of metallic superalloys.

The commercial Sylramic SiC fiber, which is the precursor for the Sylramic-iBN fiber, is produced by Dow Corning, Midland, Michigan. It is derived from polymers at low temperatures and then pyrolyzed and sintered at high temperatures using boron-containing sintering aids (ref. 1). The sintering process results in very strong fibers (>3 GPa) that are dense, oxygen-free, and nearly stoichiometric. They also display an optimum grain size that is beneficial for high tensile strength, good creep resistance, and good thermal conductivity (ref. 2). The NASA-developed treatment allows the excess boron in the bulk to diffuse to the fiber surface where it reacts with nitrogen to form an in situ boron nitride (BN) coating on the fiber surface (thus the product name of Sylramic-iBN fiber). The removal of boron from the fiber bulk allows the retention of high tensile strength while significantly improving creep resistance and electrical conductivity, and probably thermal conductivity since the grains are slightly larger and the grain boundaries cleaner (ref. 2). Also, as shown in the graph, these improvements allow the fiber to display the best rupture strength at high temperatures in air for any available SiC fiber. In addition, for CMC applications under oxidizing conditions, the formation of an in situ BN surface layer creates a more environmentally durable fiber surface not only because a more oxidation-resistant BN is formed, but also because this layer provides a physical barrier between contacting fibers with oxidation-prone SiC surface layers (refs. 3 and 4).

This year, Glenn demonstrated that the in situ BN treatment can be applied simply to Sylramic fibers located within continuous multifiber tows, within woven fabric pieces, or even assembled into complex product shapes (preforms). SiC/SiC ceramic composite panels have been fabricated from Sylramic-iBN fabric and then tested at Glenn within the Ultra-Efficient Engine Technology Program. The test conditions were selected to simulate those experienced by hot-section components in advanced gas turbine engines. The results from testing at Glenn demonstrate all the benefits expected for the Sylramic-iBN fibers. That is, the composites displayed the best thermostructural performance in comparison to composites reinforced by Sylramic fibers and by all other currently available high-performance SiC fiber types (refs. 3 and 5). For these reasons, the Ultra-Efficient Engine Technology Program has selected the Sylramic-iBN fiber for ongoing efforts aimed at SiC/SiC engine component development.

Graph of rupture strength versus stress rupture time
Rupture strength behavior for various high-performance SiC fibers at 1400 °C in air. SA, Tyranno SA fiber from UBE Industries; Hi-Nic. S, Hi-Nicalon Type S fiber from Nippon Carbon.

References

  1. Lipowitz, J., et al.: Structure and Properties of Sylramic Silicon Carbide FiberA Polycrystalline, Stoichiometric b-SiC Composition. Ceram. Eng. Sci. Proc., vol. 18, issue 3, 1997, pp. 147-157.
  2. Yun, Hee Mann; and DiCarlo, James A.: Comparison of the Tensile, Creep, and Rupture Strength Properties of Stoichiometric SiC Fibers. Ceram. Eng. Sci. Proc., vol. 20, issue 3, 1999, pp. 259-272.
  3. Yun, H.M., et al.: Tensile Behavior of SiC/SiC Composites Reinforced by Treated Sylramic SiC Fibers. Ceram. Eng. Sci. Proc., vol. 22, issue 3, 2001, pp. 521-531.
  4. DiCarlo, James A.; Yun, Hee Mann; and Brennan, John, J.: SiC/SiC Composites With Improved BN Coating on Fibers. NASA Tech Brief LEW 16864, 2000.
  5. DiCarlo, J.A., et al.: SiC/SiC Material Development Under the NASA UEET Program. Proceedings of 25th Annual Cocoa Beach Conference, restricted sessions, 2001. (Available from the NASA Glenn UEET Office.)

Glenn contact: Dr. James A. DiCarlo, 216-433-5514, James.A.DiCarlo@grc.nasa.gov
Authors: Dr. James A. DiCarlo and Dr. Hee Mann Yun
Headquarters program office: OAT
Programs/Projects: UEET
Special recognition: R&D 100 Award for 2001


next page Next article

previous page Materials


Last updated: June 2002


Responsible NASA Official: Gynelle.C.Steele@nasa.gov
216-433-8258

Point of contact for NASA Glenn's Research & Technology reports: Cynthia.L.Dreibelbis@nasa.gov
216-433-2912
SGT, Inc.

Web page curator: Nancy.L.Obryan@nasa.gov
216-433-5793
Wyle Information Systems, LLC

NASA Web Privacy Policy and Important Notices